Desenvolvimento de novas ligas quasicristalinas à base de alumínio
(Universidade Federal de São Carlos, 2018-03-21)
Quasicrystalline phases are known for presenting particular crystallographic characteristics that make them a separate group of solid materials. Most of these phases are Al-based and they form in compositions near complex ...
Estudo de ligas Ti-Nb-Zr e Ti-Nb-Mg, fundidas e na forma de recobrimentos sobre aço inoxidável, para aplicações biomédicas
(Universidade Federal de São Carlos, 2019-10-31)
In the present thesis, nanostructured coatings of Ti (100 - (20 + z)) -Nb20-Xz alloys (X = Zr and Mg) were produced by sputtering. So with that, it was possible to analyze the effect of the addition of Zr and Mg on the ...
Desenvolvimento de ligas amorfas e nanocristalinas do sistema Fe-Cr-Ni-B e suas propriedades de corrosão
(Universidade Federal de São Carlos, 2019-02-14)
Fe-Cr-Ni-B system alloys with partially amorphous structures can ensure a very attractive combination of mechanical and electrochemical properties, far superior to conventional materials. It can be used, for example, in ...
Efeito da adição de Ni na microestrutura bainítica de um novo aço para roscas e cilindros de plastificação de polímeros
(Universidade Federal de São Carlos, 2019-09-02)
Nitriding steels, such as DIN 1.8550, are used in the manufacture of screws and barrels for injection molding machines and plastic extruders. The hardening process of DIN 1.8550 occurs via water or oil quenching followed ...
Influência das condições de eletrodeposição sobre a resistência a corrosão, susceptibilidade à fragilização por hidrogênio e à corrosão sob tensão do aço ABNT – 4340 revestido com liga Zn/Ni
(Universidade Federal de São Carlos, 2011-01-28)
Zinc-nickel alloys were electrodeposited on ABNT 4340 high strength steel in chloride acid media. The effect of the electrolyte composition and electroplating conditions on cathodic efficiency, chemical composition, ...
Simulação computacional do início da precipitação induzida por deformação durante o processamento termomecânico de um aço microligado ao nióbio em resfriamento contínuo
(Universidade Federal de São Carlos, 2019-03-29)
Improving the steel processing is a major focus of the metallurgical industry because the need of materials and products with lower weight and more strength, in addition to increasingly stringent specifications imposed by ...
Caracterização microestrutural e mecânica da liga AA2024 conformada por spray e processada termomecanicamente
(Universidade Federal de São Carlos, 2019-03-22)
This work aimed to evaluate the possibility of combining spray forming processing with mechanical processing techniques (for instance, extrusion, rotary forging, and equal-channel angular pressing (ECAP)) to be used as ...