Comportamento de oxidação em temperaturas elevadas de ligas NiTiNb com efeito memória de forma
(Universidade Federal de São Carlos, 2021-09-10)
Shape memory alloys (SMA) of the Nickel-Titanium (NiTi) system are currently the most commercially important, due to their excellent mechanical properties, high shape recovery and biocompatibility. Such a unique set of ...
Estudo das propriedades mecânicas do aço ao boro 50B35 com diferentes tamanhos de grãos
(Universidade Federal de São Carlos, 2015-07-22)
Boron steel has excellent hardenability due to the addition of small quantities of
boron. Boron atoms reduces the nucleation rate of ferrite and bainite [1]. It is
known that austenitizing temperature and time and cooling ...
Fadiga de ligas de titânio com superfície modificada com nanotubos
(Universidade Federal de São Carlos, 2016-07-29)
Among the surface modification techniques to improve the fixation, biocompatibility and corrosion resistance of titanium implants, one of the most recent and promising is the electrochemical anodization in electrolytes ...
Avaliação de corrosão sob tensão e corrosão-fadiga do aço API 5L X70 em solução etanólica sintética
(Universidade Federal de São Carlos, 2022-04-07)
API X70 steel has been widely used in Brazil for the manufacture of ethanol transport pipelines, however, a recognized problem in carbon steel pipes exposed to ethanol is stress corrosion cracking (SCC) and, in addition, ...
Panorama das atividades de extensão do departamento de engenharia de materiais da UFSCar e oportunidades para sua curricularização na graduação
(Universidade Federal de São Carlos, 2023-01-23)
Guidelines for service-learning’s curricular use in graduation ensures 10% of the
total student workload of undergraduate courses to service-learning activity. This
policy has potential to offer benefits in mutual ...
Solidificação, microestrutura e propriedades mecânicas da liga de alumínio 6061 com 1,4%p Fe processada por conformação por spray e extrusão a quente
(Universidade Federal de São Carlos, 2017-11-24)
The 6xxx series aluminum alloys are wrought alloys which belongs to the MgSi class and can be heat treated, have a good workability and a good mechanical resistance / weight ratio. A great challenge is to avoid impurity ...
Desenvolvimento de novas ligas quasicristalinas à base de alumínio
(Universidade Federal de São Carlos, 2018-03-21)
Quasicrystalline phases are known for presenting particular crystallographic characteristics that make them a separate group of solid materials. Most of these phases are Al-based and they form in compositions near complex ...
Pesquisa em consolidação do fechamento de vazios internos em produtos forjados no aço W.Nr. 1.2738 modificado
(Universidade Federal de São Carlos, 2018-11-23)
During steel ingot solidification, internal voids are expected to be formed in its interior. Such voids, if they stay in the final product after the forging step, will hurt the performance and properties of the final ...
Simulação computacional do início da precipitação induzida por deformação durante o processamento termomecânico de um aço microligado ao nióbio em resfriamento contínuo
(Universidade Federal de São Carlos, 2019-03-29)
Improving the steel processing is a major focus of the metallurgical industry because the need of materials and products with lower weight and more strength, in addition to increasingly stringent specifications imposed by ...
Caracterização microestrutural e mecânica da liga AA2024 conformada por spray e processada termomecanicamente
(Universidade Federal de São Carlos, 2019-03-22)
This work aimed to evaluate the possibility of combining spray forming processing with mechanical processing techniques (for instance, extrusion, rotary forging, and equal-channel angular pressing (ECAP)) to be used as ...